The influence of temperature on the structure of Cd-doped ZnO nanopowders
The influence of temperature on the structure of Cd-doped ZnO nanopowders
 
الموضوع : فيزياء 
لغة الوثيقة : الانجليزية 
المستخلص : A new and facile method has been used for preparation of CdZnO nanopowder. The prepared nanopowder was in the form of binary mixture of CdO and ZnO until annealing temperature 400 °C. When the annealing temperature increased above 400 °C the structure of the nanopowder was changed from binary mixture to a single hexagonal phase. Thermogravimetry/differential thermal analysis (TG-DTA), X-ray diffraction (XRD) and transmission electron microscopy (TEM) were used to follow the change in the microstructure and morphology of the prepared nanopowders at different temperatures. The effect of calcination temperature on the growth dynamics of CdZnO nanopowder showed that the dynamic growth index was 1.13 below 400 °C and 0.5 above it. This indicates that the rate of the grain growth was very fast especially at calcination temperature range 400-750 °C. 
ردمد : 09258388 
اسم الدورية : Journal of Alloys and Compounds 
المجلد : 491 
العدد : 1-2 
سنة النشر : 2010 هـ
2010 م
 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Saturday, February 6, 2010 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
وليد محمودMahmoud, Waleed Wباحثدكتوراهw_e_mahmoud@yahoo.com
أحمد عبدالله الغامديAL-GHAMDI, A AباحثدكتوراهAGAMDI@kau.edu.sa
صالح هديهد الحنيطيAL-HENITI, S Hباحثدكتوراهsalheniti@kau.edu.sa
سعيد سعد الاميرAl-Ameer, Saeed Sباحثدكتوراهssaameer@yahoo.com

الملفات

اسم الملفالنوعالوصف
 25151.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث