THE EFFECT OF FLUORIDERECHARGINGOFDIFFERENT IONOMER BASED RESTORATIONS ON ITS MECHANICAL PERFORMANCE
THE EFFECT OF FLUORIDERECHARGINGOFDIFFERENT IONOMER BASED RESTORATIONS ON ITS MECHANICAL PERFORMANCE
 
لغة الوثيقة : الانجليزية 
المستخلص : The Study investigated the diametral tensile strength (DTS) of three ionomer based restorarive materials (Fuji II, Fuji II LC and Fuji IX) after the application of two fluoride recharging agents(1.23% APF gel and 0.4 % SnF2gel( at time intervals: 24 hours and 28 days. A total of 90 samples were prepared using split Teflon moulds and stored in distilled water at room temperature. The diametral tensile strength was tested using a universal testing machine at a crosshead speed of 0.5 mm/min, and the maximum applied load was recorded and the (DTS( was calculated in (MPa. (One way analysis of variance )Procedure ANOVA of SAS) followed by Duncan's multiple Range Test were used to test the effect of topical fluoride application on The (DTS) within each restorative material. The results of this study showed that the (DTS) of Fuji II after 24 hours was increased with both recharging gels, APF gel had no effect on DTS for Fuji II LC and DTS for Fuji IX was decreased. SnF2gel showed no effect on the DTS of Fuji IX and decreased it for Fuji II LC. After 28 days: APF gel had decreased DTS for Fuji II, no effect on DTS of Fuji II LC and increased it of Fuji IX. While, SnF2gel had no effect on DTS of both Fuji II & Fuji II LC but increased DTS of Fuji IX. By increasing the storage period up 102Xdays: there was an increase of DTS for both Fuji II and Fuji II LC and decreased the DTS for Fuji IX. 
ردمد : 9484-0070 
اسم الدورية : EGYPTIAN DENTAL JOURNAL 
المجلد : 55 
العدد : 1 
سنة النشر : 2009 هـ
2009 م
 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Wednesday, June 16, 2010 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
فاضل عثمانOthman, Fadel باحث رئيسيدكتوراه 
عمرو Abdelazizعبد العزيز, Amr باحث مشاركدكتوراه 
عبد الغني ميرهMira, Abdel Ghanni باحث مشاركدكتوراه 

الملفات

اسم الملفالنوعالوصف
 27046.pdf pdf 
 27047.pdf pdf 

الرجوع إلى صفحة الأبحاث